氢氧化钾由于其强碱性和腐蚀性，在化工等行业有着重要的应用。它还可以作为各种试剂应用于不同领域，如干燥剂、吸收剂、耐火胶粘剂等。那么，我们就来看看它的耐火胶粘剂的制备方法。
Potassium hydroxide is widely used in chemical industry because of its strong alkalinity and corrosiveness. It can also be used as a variety of reagents in different fields, such as desiccant, absorbent, refractory adhesive, etc. So, let's take a look at the preparation method of its refractory adhesive.
1.耐火胶粘剂的研制
1. Development of refractory adhesive
①耐火液体的制备方法：在反应罐中依次加入8kg粒状氢氧化钾、7kg粉状碳酸钠（纯碱）（朝日硝酸盐公司生产）、30kg金属硅化物，再加入60L水。在反应罐中，自然反应开始，剧烈反应从下部产物开始，对流从下部向上部发生。当反应温度在80℃～90℃之间时，反应活跃。反应温度不高于92℃。通过分离固体可获得约48l（70kg）的难熔液体。
① Preparation method of refractory liquid: 8kg granular potassium hydroxide, 7kg powdered sodium carbonate (soda) (Asahi nitrate company), 30kg metal silicide and 60L water are successively added into the reaction tank. In the reaction tank, the natural reaction starts, the violent reaction starts from the lower product, and the convection occurs from the lower part to the upper part. When the reaction temperature is between 80 ℃ and 90 ℃, the reaction is active. The reaction temperature is not higher than 92 ℃. About 48l (70kg) of refractory liquid can be obtained by solid separation.

残余固体为金属硅化物。如果用水清洗，大约22公斤的金属硅化物残留。在该残余金属硅化物块中，添加约8kg的金属硅化物块，并且金属硅化物的总量为30kg，其被供应给二次反应。
The residual solid is metal silicide. If washed with water, about 22 kg of metal silicide remains. In the residual metal silicide block, about 8 kg of metal silicide block is added, and the total amount of metal silicide is 30 kg, which is supplied to the secondary reaction.
与刚开始的反应相同，向反应罐中加入8kg粒状碳酸钠和7kg粉状碳酸钠（纯碱）（旭硝子公司生产），然后依次加入22kg残余金属硅化物块和8kg新的金属硅化物块，加水60L，开始制备耐火液体的二次反应。在制备过程中，按照先加入颗粒状氢氧化钾，再加入粉状碳酸钠（纯碱），再加入金属硅化物块，再加水的顺序，反应从较低的产物开始，形成上下对流型活性反应，因此制备的耐火液体具有较好的性能。
Similar to the initial reaction, 8kg granular sodium carbonate and 7kg powdered sodium carbonate (soda) (produced by Xuni subsidiary) were added to the reaction tank, then 22kg residual metal silicide block and 8kg new metal silicide block were added in turn, and 60L water was added to start the secondary reaction of preparing refractory liquid. In the preparation process, according to the order of adding granular potassium hydroxide, then adding powdered sodium carbonate (soda), then adding metal silicide block, and then adding water, the reaction starts from the lower product, forming the up-down convection type active reaction, so the prepared refractory liquid has better performance.
②耐火胶的制备：向反应罐中分别加入耐火液、切旧报纸（也可使用其他旧报纸）、稻壳和棉花，搅拌均匀，制成耐火材料。
② Preparation of refractory adhesive: add refractory liquid, cut old newspaper (other old newspaper can also be used), rice husk and cotton into the reaction tank, mix them evenly to make refractory material.
2.如果涂有耐火液体，则涂有耐火液体的纸板在接近1000℃的火焰下燃烧30分钟不会燃烧。将耐火胶黏剂混合物加压脱水至含水量45%，在180℃加压1h制备轻质耐火材料。耐火材料在1500℃下观察30分钟。10分钟后，耐火材料表面玻璃化。燃烧30分钟后，耐火材料被切割。玻璃化深度只有0.8毫米，火没有进入耐火材料。此外，耐火材料具有良好的隔音和抗冲击性能。它能切割、锯、钉、螺丝等加工性能与木材相似。
2. If coated with fire-resistant liquid, the paperboard coated with fire-resistant liquid will not burn after burning for 30 minutes under a flame close to 1000 ℃. The refractory adhesive mixture was dehydrated to 45% water content under pressure, and the lightweight refractory was prepared at 180 ℃ for 1 h. The refractories were observed at 1500 ℃ for 30 minutes. After 10 minutes, the refractory surface vitrified. After burning for 30 minutes, the refractory is cut. The depth of vitrification was only 0.8 mm, and the fire did not enter the refractory. In addition, refractories have good sound insulation and impact resistance. It can cut, saw, nail, screw and other processing performance is similar to wood.